Influence of fluorine on the synthesis of anatase TiO2for photocatalytic partial oxidation: Are exposed facets the main actors?
2018
Anatase TiO2 samples were synthesized in the presence of different amounts of HF acid with the aim of understanding the effect of the presence of fluorine on the photocatalytic activity. It is well known that the presence of fluoride ions influences the photocatalytic performance by adsorption on the surface of TiO2 and that they are capping agents in the control of specific exposed facets. The samples were characterized by X-ray diffraction (XRD), Raman spectroscopy, nitrogen adsorption–desorption measurements, scanning electron microscopy (SEM), transmission electron microscopy (TEM), UV-vis spectrophotometry, and X-ray photoelectron spectroscopy (XPS). The photocatalytic activity was eva…
Extraordinary Performance of Carbon‐Coated Anatase TiO 2 as Sodium‐Ion Anode
2015
The synthesis of in situ polymer‐functionalized anatase TiO2 particles using an anchoring block copolymer with hydroxamate as coordinating species is reported, which yields nanoparticles (≈11 nm) in multigram scale. Thermal annealing converts the polymer brushes into a uniform and homogeneous carbon coating as proven by high resolution transmission electron microscopy and Raman spectroscopy. The strong impact of particle size as well as carbon coating on the electrochemical performance of anatase TiO2 is demonstrated. Downsizing the particles leads to higher reversible uptake/release of sodium cations per formula unit TiO2 (e.g., 0.72 eq. Na+ (11 nm) vs only 0.56 eq. Na+ (40 nm)) while the …
The role of water in the photocatalytic degradation of acetonitrile and toluene in gas-solid and liquid-solid regimes
2006
Photocatalytic degradation of acetonitrile and toluene was carried out both in gas-solid and in liquid-solid regimes by using commercialTiO2samples (Merck and Degussa P25). The investigation was mainly aimed to study the influence of water present in the reaction environment on the mechanism and degradation rate of two probe molecules. In gas-solid regime, the reacting mixture consisted of toluene or acetonitrile, oxygen, nitrogen, and water vapour. The main degradation product of toluene wasCO2with small amounts of benzaldehyde. In the presence of water vapour, the activity ofTiO2Merck remained stable but greatly decreased if water was absent.TiO2Degussa P25 continuously deactivated, even …